Ndi chitukuko cha sayansi, kusindikizidwa dera bolodiwasanduka singasiyanitsidwe pakompyuta chigawo, mabuku dera bolodi wakhala anadzatchedwa monga zamagetsi substrate.Traditional gawo lapansi zochita kupanga kwa Al2O3, ndi SiC, BeO ndi AlN gawo lapansi, zinthuzi mu madutsidwe ikukhudzana kupinda mphamvu ndi matenthedwe koyefishienti kuwonjezeka ali ndi ntchito zabwino, tsopano chimagwiritsidwa ntchito m'mafakitale a MCM substrate.The kuphunzira Ceramic zinthu PCB ndi micron Al2O3 ndi CaZrO3 monga nkhani yaikulu yaiwisi, ntchito kukana ng'anjo sintering pakachitsulo carbide, ndi kufufuza wachibale osalimba, dielectric zonse ndi katundu dielectric imfa.
1.Relative kachulukidwe kusanthula 
The influence of the relative density of alumina ceramic integrated circuit substrate with different micron Al2O3 and nano CaZrO3 powder was added.By a figure known as the temperature increases, the relative density with the increase of substrate material, temperature of 1100 ℃ maximum.When micron Al2O3 content is 60 wt %, the adding amount of nano ZrO2 is 10 wt %, the relative density of alumina ceramic pcb substrate integrated material relative to other formula is the largest, the sample is relatively dense, is beneficial to integration of alumina ceramics substrate material mechanics performance improvement.
2.Dielectric kusanthula zonse 
The above is the dielectric constant of the Ceramic PCB material with the curve of sintering temperature.It can be seen that as the temperature rises, its dielectric constant increases.When the temperature reached 1100 ℃, the dielectric constant peak.When the addition of micron Al2O3 was changed from 50 wt% to 65 wt %, and the addition of nano-cazro3 was changed from 20 wt% to 5 wt %, the dielectric constant of the alumina integrated electric subgrade plate was first increased and then decreased.When the content of micron Al2O3 was 60 wt% and the content of nano CaZrO3 was 10 wt %, the sample performance was the best.This is because the factors that influence the dielectric constant are multifaceted, as long as the chemical composition of the formulation is involved, the more the alkali metal ion oxide content is, the greater the permittivity is.In addition, the thermal exercise of the ions and dipoles in the process of rising temperature increases, resulting in an increase in the permittivity.
3.Dielectric imfa kusanthula 
The above is the dielectric loss of the ceramic pcb cesubstrate material with the sintering temperature curve.As the temperature increases, the dielectric loss gradually decreases.When the micron Al2O3 in 50 wt % 65 wt % change between nano CaZrO3 between 20 wt % to 5 wt % change, dielectric loss reduced after increased first, when the micron Al2O3 content is 60 wt %, nano CaZrO3 amount to 10 wt %, and when the sintering temperature is 1100 ℃, the dielectric loss value of the minimum sample after sintering.
The dielectric loss of the ceramic pcb material is caused by the internal electron, ion drain and space charge polarization, and the smaller the volume resistivity of the material, the larger the dielectric loss.Of the existence of samples CaZrO3 Ca (superscript 2 +) ions of other low price and tetravalent Zr ions produce depressive effect, make the dielectric loss of samples increased, the Na2O and the existence of K2O, makes the ion K and Na ions as a result of the action of the double effect of alkali, make the network combined with close, so the sample dielectric loss less.